Cationic electrodeposition coating composition

ABSTRACT

A cationic electrodeposition coating composition including amino group-containing modified epoxy resin (A), blocked polyisocyanate curing agent (B), phenol resin (C), metal compound (D), and nitrogen oxide ion (E), wherein the metal compound (D) is contained in an amount of 10 to 10,000 ppm calculated as metal and the nitrogen oxide ion (E) is contained in an amount of 50 to 10,000 ppm, relative to the mass of the cationic electrodeposition coating composition. The cationic electrodeposition coating composition exhibits excellent anti-corrosion properties when coated onto untreated steel sheets.

TECHNICAL FIELD

The present invention relates to a cationic electrodeposition coating composition that exhibits, without containing toxic substances such as lead compounds, chromium compounds, etc., excellent anti-corrosion properties, particularly on untreated steel sheets.

BACKGROUND ART

Because of their excellent throwing power and low environmental impact, cationic electrodeposition coating compositions are widely used for various applications such as undercoating compositions for automobiles etc. Cationic electrodeposition coating compositions that contain lead compounds and/or chromium compounds, e.g., lead chromate, basic lead silicate, and strontium chromate, have been suggested.

However, because of problems with environmental pollution, the use of toxic compounds such as lead compounds and chromium compounds is restricted; and a cationic electrodeposition coating composition that uses a non-toxic or low-toxic rust-preventive pigment, and provides excellent anti-corrosion properties without containing harmful compounds has been developed and is now in use.

For example, Patent Literature 1 discloses a cationic electrodeposition coating composition that comprises (A) a cationic amine modified epoxy resin, (B) a blocked polyisocyanate, and (C) a phosphorous acid divalent or trivalent metal salt, the purpose thereof being to improve anti-corrosion properties without containing lead. Patent Literature 2 discloses a zirconium compound-containing cationic electrodeposition coating composition that exhibits excellent anti-corrosion properties without containing lead.

Patent Literatures 1 and 2 disclose that a film formed on a surface-treated steel sheet has excellent anti-corrosion properties even without containing toxic substances such as lead compounds and chromium compounds. However, an electrodeposition coating film formed on a surface-untreated steel sheet has insufficient anti-corrosion properties.

Patent Literature 3 discloses a cationic electrodeposition coating composition comprising a cationic amine modified epoxy resin, a blocked polyisocyanate, and a zirconium salt, the purpose thereof being to improve rust preventive properties to the greatest extent possible. Patent Literature 3 teaches that the composition can provide, even without containing harmful compounds such as lead compounds, chromium compounds, etc., an electrodeposition coating film having excellent anti-corrosion properties on a surface-untreated steel sheet.

However, under severely corrosive conditions, the aforementioned electrodeposition coating film formed on the surface-untreated steel sheet exhibits insufficient anti-corrosion properties; in particular, an electrodeposition coating film having a thickness of 15 μm or less (when dried) that is formed on an untreated steel sheet exhibits insufficient anti-corrosion properties. Accordingly, further improvement has been desired.

CITATION LIST Patent Literature

-   [PTL 1] Japanese Unexamined Patent Publication No. H9-241546 -   [PTL 2] Japanese Unexamined Patent Publication No. 2000-290542 -   [PTL 3] Japanese Unexamined Patent Publication No. 2009-46628

SUMMARY OF INVENTION Technical Problem

The object of the present invention is to make, without using lead compounds, chromium compounds, and like toxic substances, a cationic electrodeposition coating composition that exhibits excellent anti-corrosion properties on an untreated steel sheet, in particular a cationic electrodeposition coating composition that exhibits excellent anti-corrosion properties on an untreated steel sheet even when the formed coating film is an electrodeposition coating film having a thickness of 15 μm or less (when dried).

Solution to Problem

The present inventors have conducted extensive research to achieve the above object, and found that the object can be attained by a cationic electrodeposition coating composition comprising amino group-containing modified epoxy resin (A), blocked polyisocyanate curing agent (B), phenol resin (C), metal compound (D), and nitrogen oxide ion (E). The present invention was thus accomplished.

Specifically, the present invention provides the following items.

Item 1

A cationic electrodeposition coating composition comprising amino group-containing modified epoxy resin (A), blocked polyisocyanate curing agent (B), phenol resin (C), metal compound (D), and nitrogen oxide ion (E);

the cationic electrodeposition coating composition comprising the metal compound (D) in an amount of 10 to 10,000 ppm calculated as metal (on a metal mass basis), and the nitrogen oxide ion (E) in an amount of 50 to 10,000 ppm, relative to the mass of the cationic electrodeposition coating composition,

the amino group-containing modified epoxy resin (A) being a resin obtainable by reacting modified epoxy resin (A1) having an epoxy equivalent of 500 to 2,500 and amine compound (A2),

the modified epoxy resin (A1) being obtainable by reacting diepoxy compound (a1), epoxy resin (a2) having an epoxy equivalent of 170 to 500, and bisphenol compound (a3),

the diepoxy compound (a1) being compound (1) represented by Formula (1) below,

wherein R¹ is the same or different, and each represents a hydrogen atom or a C₁₋₆ alkyl group; R² is the same or different, and each represents a hydrogen atom or C₁₋₂ alkyl group, and m and n, which represent the number of repeating units of the portion having an alkylene oxide structure, are integers where m+n=1 to 20, and/or compound (2) represented by Formula (2) below,

wherein R³ represents a hydrogen atom or C₁₋₆ alkyl group, X is an integer of 1 to 9, and Y is an integer of 1 to 50; when Y is 2 or more, each R³ in the repeating unit is the same or different, and the metal compound (D) being a compound of at least one metal (d) selected from the group consisting of zirconium, titanium, cobalt, vanadium, tungsten, molybdenum, copper, indium, zinc, aluminum, bismuth, yttrium, lanthanoids, alkali metals, and alkaline earth metals. Item 2 The cationic electrodeposition coating composition according to Item 1, wherein the amino group-containing modified epoxy resin (A) is contained in an amount of 30 to 75 parts by mass, the blocked polyisocyanate curing agent (B) is contained in an amount of 10 to 40 parts by mass, and the phenol resin (C) is contained in an amount of 3 to 35 parts by mass, based on the total solids mass (100 parts by mass) of the amino group-containing modified epoxy resin (A), blocked polyisocyanate curing agent (B), and phenol resin (C). Item 3 The cationic electrodeposition coating composition according to Item 1 or 2, wherein the modified epoxy resin (A1) is obtainable by reacting 1 to 35 mass % of the diepoxy compound (a1), 10 to 80 mass % of the epoxy resin (a2), and 10 to 60 mass % of the bisphenol compound (a3), based on the total solids mass of the diepoxy compound (a1), epoxy resin (a2), and bisphenol compound (a3). Item 4 The cationic electrodeposition coating composition according to any one of Items 1 to 3, wherein R¹ in the Formula (1) or R³ in the Formula (2) is a methyl group or hydrogen atom. Item 5 The cationic electrodeposition coating composition according to any one of Items 1 to 4, wherein the metal compound (D) consists of a zirconium compound, or comprises at least one compound selected from the group consisting of zirconium compounds and titanium compounds, and a compound of at least one metal selected from the group consisting of cobalt, vanadium, tungsten, molybdenum, copper, indium, zinc, aluminum, bismuth, yttrium, lanthanoids, alkali metals, and alkaline earth metals. Item 6 The cationic electrodeposition coating composition according to any one of Items 1 to 5, wherein the solids content of the cationic electrodeposition coating composition is 5 to 40 mass %. Item 7 A coated article obtainable by immersing a metal substrate in an electrodeposition coating composition bath containing the cationic electrodeposition coating composition according to any one of Items 1 to 6, and performing electrodeposition coating.

Advantageous Effects of Invention

According to the cationic electrodeposition coating composition of the present invention, a coated article that has excellent anti-corrosion properties on an untreated steel sheet, in particular, excellent anti-corrosion properties on an untreated steel sheet even when the formed coating film is a thin film with a thickness of 15 μm or less (when dried), can be obtained without containing toxic metals such as lead compounds, chromium compounds, etc. For this reason, the cationic electrodeposition coating composition of the present invention is useful for the electrodeposition coating of automobile bodies and parts, electrical appliances, etc.

There is no particular limitation on the method for producing a coating film using the cationic electrodeposition coating composition of the present invention. If a two-step method including immersion and electrodeposition is applied, a film (lower layer) mainly comprising inorganic components can be first formed by allowing metal compound (D) to be selectively deposited on the substrate, and then a film (upper layer) mainly comprising organic components can be formed by allowing resin components etc. that comprise amino group-containing modified epoxy resin (A) and blocked polyisocyanate curing agent (B) to be deposited on the film (lower layer). Thus, the lower layer that contains metal oxide having passivation can be formed on the surface of a metal substrate such as an untreated steel sheet, which contributes to the inhibition of corrosion under the film. Further, the addition of phenol resin (C) can improve adhesion with the substrate, which ensures a further improvement in anti-corrosion properties.

Still further, diepoxy compound (a1) used in amino group-containing modified epoxy resin (A) can help to provide a coated article that has excellent bath (liquid) stability and anti-corrosion properties over time even though the cationic electrodeposition coating composition includes metal compound (D) and nitrogen oxide ion (E).

DESCRIPTION OF EMBODIMENTS

The present invention relates to a cationic electrodeposition coating composition that comprises amino group-containing modified epoxy resin (A), blocked polyisocyanate curing agent (B), phenol resin (C), metal compound (D), and nitrogen oxide ion (E), wherein metal compound (D) is contained in an amount of 10 to 10,000 ppm calculated as metal, and nitrogen oxide ion (E) is contained in an amount of 50 to 10,000 ppm, relative to the mass of the cationic electrodeposition coating composition.

The present invention is detailed below.

Amino Group-Containing Modified Epoxy Resin (A)

Amino group-containing modified epoxy resin (A) for use in the present invention is a resin obtainable by reacting modified epoxy resin (A1) having an epoxy equivalent of 500 to 2,500 with amine compound (A2).

The aforementioned modified epoxy resin (A1) is a resin obtainable by reacting diepoxy compound (a1), i.e., compound (1) represented by Formula (1) and/or compound (2) represented by Formula (2); epoxy resin (a2) having an epoxy equivalent of 170 to 500; and bisphenol compound (a3).

Modified Epoxy Resin (A1) Having an Epoxy Equivalent of 500 to 2,500:

The aforementioned modified epoxy resin (A1) is a modified epoxy resin having an epoxy equivalent of 500 to 2,500 that is obtainable by reacting specific diepoxy compound (a1), epoxy resin (a2) having an epoxy equivalent of 170 to 500, and bisphenol compound (a3).

Diepoxy Compound (a1)

As diepoxy compound (a1), compound (1) represented by Formula (1) can be used,

wherein R¹ is the same or different, and each represents a hydrogen atom or a C₁₋₆ alkyl group; R² is the same or different, and each represents a hydrogen atom or a C₁₋₂ alkyl group; m and n, which represent the number of repeating units of the portion having an alkylene oxide structure, are integers where m+n=1 to 20.

In Formula (1), when at least either m or n represents 2 or more, each R¹ in the repeating unit “m”, and each R¹ in the repeating unit “n” may be the same or different.

Compound (1) can be produced by adding alkylene oxide represented by Formula (3) below,

wherein R⁴ represents a hydrogen atom or a C₁₋₆ alkyl group, to bisphenol A, bisphenol F, etc., to obtain a hydroxy-terminated polyether compound, and then allowing the polyether compound to react with epihalohydrin to obtain a diepoxy compound.

Examples of alkylene oxide represented by Formula (3) include ethylene oxide, propylene oxide, butylene oxide, hexylene oxide, octylene oxide and like C₂₋₈ alkylene oxides.

Of these, ethylene oxide (compound in which R⁴ in Formula (3) is a hydrogen atom) and propylene oxide (compound in which R⁴ in Formula (3) is a methyl group) are preferable.

Compound (2):

As diepoxy compound (a1), compound (2) represented by Formula (2) can be used,

wherein R³ represents a hydrogen atom or a C₁₋₆ alkyl group; X represents 1 to 9; and Y is an integer of 1 to 50. When Y is 2 or more, R³ in the repeating unit may be the same or different.

Examples of the method for producing compound (2) include method (1) in which alkylene oxide represented by Formula (2) is subjected to ring-opening polymerization using alkylene glycol as a starting material, thereby obtaining hydroxyl-terminated polyalkylene oxide, and the polyalkylene oxide is allowed to react with epihalohydrin to form a diepoxy compound.

Another example of the method for producing compound (2) is method (2) in which alkylene glycol represented by Formula (4) or polyether diol obtained by condensing two or more alkylene glycol molecules by dehydration, is allowed to react with epihalohydrin to form a diepoxy compound,

wherein R⁵ represents a hydrogen atom or a C₁₋₆ alkyl group, and X is an integer of 1 to 9.

Examples of alkylene glycol represented by Formula (4) used herein include ethylene glycol, propylene glycol, trimethylene glycol, 1,4-butanediol, 1,3-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,8-octanediol, 1,9-nonandiol and like C₂₋₁₀ alkylene glycols.

Examples of diepoxy compound (a1) represented by Formula (1) or Formula (2) include Denacol EX-850, Denacol EX-821, Denacol EX-830, Denacol EX-841, Denacol EX-861, Denacol EX Denacol EX-920, Denacol EX-931 (produced by Nagase ChemteX Corporation); Glyci-ale PP-300P and Glyci-ale BPP-350 (produced by Sanyo Chemical Industries, Ltd.); etc. As diepoxy compound (a1), compounds (1) and (2) may be used in combination.

Epoxy Resin (a2) Having an Epoxy Equivalent of 170 to 500

In the present invention, epoxy resin (a2) having an epoxy equivalent of 170 to 500 (hereinafter sometimes simply referred to as epoxy resin (a2)) for use in the production of modified epoxy resin (A1) having an epoxy equivalent of 500 to 2,500 includes compounds having two or more epoxy groups per molecule, and an epoxy equivalent of 170 to 500, preferably 170 to 400, excluding diepoxy compound (a1), i.e., compound (1) represented by Formula (1) and compound (2) represented by Formula (2). Suitable epoxy resin (a2) has a number average molecular weight of 340 to 1,500, and preferably 340 to 1,000. In particular, epoxy resin (a2), which can be obtained by reacting a polyphenol compound with epihalohydrin, is preferable.

The “number average molecular weight” herein is a value determined according to the method of JIS K 0124-83, from a chromatogram measured by gel permeation chromatograph, based on the molecular weight of standard polystyrene. For a gel permeation chromatograph, “HLC8120GPC” (produced by Tosoh Corporation) was used. The measurement was conducted using four columns, “TSK GEL G-4000HXL”, “TSK GEL G-3000HXL”, “TSK GEL G-2500HXL”, and “TSK GEL G-2000HXL” (trade names; produced by Tosoh Corporation), under the following conditions: mobile phase: tetrahydrofuran, measuring temperature: 40° C., flow rate: 1 ml/min, and detector: RI.

Examples of polyphenol compounds used for forming such epoxy resins include bis(4-hydroxyphenyl)-2,2-propane (bisphenol A), bis(4-hydroxyphenyl)methane (bisphenol F), bis(4-hydroxycyclohexyl)methane (hydrogenated bisphenol F), 2,2-bis(4-hydroxycyclohexyl)propane (hydrogenated bisphenol A), 4,4′-dihydroxybenzophenone, bis(4-hydroxyphenyl)-1,1-ethane, hydroxyphenyl)-1,1-isobutane, bis(4-hydroxy-2 or 3-tert-butyl-phenyl)-2,2-propane, bis(2-hydroxynaphthyl)methane, tetra(4-hydroxyphenyl)-1,1,2,2-ethane, 4,4′-dihydroxydiphenylsulfone, phenol novolac, cresol novolac, etc.

Of the epoxy resins obtainable by reacting a polyphenol compound with epichlorohydrin, those of the following Formula (5) derived from bisphenol A are preferable,

wherein n is 0 to 2.

Examples of commercial products of such epoxy resins include those available from Japan Epoxy Resins Co., Ltd. under the trade names of jER828EL and jER1001.

Bisphenol Compound (a3):

Examples of bisphenol compound (a3) include those represented by Formula (6) below,

wherein R⁶ and R⁷ each represents a hydrogen atom or a C₁₋₆ alkyl group; and R⁸, R⁹, R¹⁰, R¹¹, R¹², R¹³, R¹⁴, and R¹⁵ are the same or different, and each represents a hydrogen atom or a C₁₋₆ alkyl group.

Specific examples thereof include bis(4-hydroxyphenyl)-2,2-propane (bisphenol A), bis(4-hydroxyphenyl)methane (bisphenol F), etc.

In general, modified epoxy resin (A1) having an epoxy equivalent of 500 to 2,500 can be produced by mixing diepoxy compound (a1), epoxy resin (a2) having an epoxy equivalent of 170 to 500, and bisphenol compound (a3), and reacting these three compounds in the presence of a suitably selected reaction catalyst such as dimethylbenzylamine, tributylamine, or like tertiary amines; tetraethylammonium bromide, tetrabutylammonium bromide or like quaternary ammonium salts, at a reaction temperature of about 80° C. to 200° C., and preferably about 90° C. to 180° C., for 1 to 6 hours, and preferably 1 to 5 hours.

Examples of methods for producing modified epoxy resin (A1) are as follows (Methods 1 to 3).

1. A method in which diepoxy compound (a1), epoxy resin (a2) having an epoxy equivalent of 170 to 500, and bisphenol compound (a3) are all mixed and reacted with each other to produce modified epoxy resin (A1) having an epoxy equivalent of 500 to 2,500.

2. A method in which diepoxy compound (a1) and bisphenol compound (a3) are reacted to yield a reaction mixture, after which epoxy resin (a2) having an epoxy equivalent of 170 to 500 is added and reacted with the reaction mixture to produce modified epoxy resin (A1) having an epoxy equivalent of 500 to 2,500. 3. A method in which epoxy resin (a2) having an epoxy equivalent of 170 to 500 is reacted with bisphenol compound (a3) to yield a reaction mixture, after which diepoxy compound (a1) is added and reacted with the reaction mixture to produce modified epoxy resin (A1) having an epoxy equivalent of 500 to 2,500. The reaction state can be traced by epoxy value.

In the production of modified epoxy resin (A1), the proportion of diepoxy compound (a1) is preferably 1 to 35 mass %, and more preferably 2 to 30 mass %, based on the total solids mass of the components for forming modified epoxy resin (A1), i.e., diepoxy compound (a1), epoxy resin (a2) having an epoxy equivalent of 170 to 500, and bisphenol compound (a3). The proportion in the above range is preferable to attain excellent water dispersibility of amino group-containing modified epoxy resin (A) and excellent bath (liquid) stability even when the cationic electrodeposition coating composition includes metal compound (D) and nitrogen oxide ion (E), and to improve anti-corrosion properties on an untreated steel sheet, particularly anti-corrosion properties on an untreated steel sheet even when the formed coating film is a thin film having a thickness of 15 μm or less (when dried).

Further, to provide a coating film having excellent anti-corrosion properties on an untreated steel sheet, particularly when the formed coating film has a thickness of 15 μm or less (when dried), it is preferable that the proportion of epoxy resin (a2) having an epoxy equivalent of 170 to 500 be 10 to 80 mass %, particularly 15 to 75 mass %, and the proportion of bisphenol compound (a3) be 10 to 60 mass %, particularly 15 to 50 mass %.

In the above production, an organic solvent may be optionally used. Examples thereof include toluene, xylene, cyclohexane, n-hexane and like hydrocarbon-based solvents; methyl acetate, ethyl acetate, butyl acetate and like ester-based solvents; acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl amyl ketone and like ketone-based solvents; dimethyl formamide, dimethyl acetamide and like amide-based solvents; methanol, ethanol, n-propanol, isopropanol and like alcohol-based solvents; phenylcarbinol, methylphenylcarbinol and like aromatic alkyl alcohol-based solvents; ethylene glycol monobutyl ether, diethylene glycol monoethyl ether and like ether alcohol-based solvents; and mixtures thereof, etc.

Amine Compound (A2)

Amino group-containing modified epoxy resin (A) can be obtained by subjecting modified epoxy resin (A1) to an addition reaction with amine compound (A2). Examples of amine compound (A2) include mono- or dialkylamines such as monomethylamine, dimethylamine, monoethylamine, diethylamine, monoisopropylamine, diisopropylamine, monobutylamine, dibutylamine, etc.; alkanolamines such as monoethanolamine, diethanolamine, mono(2-hydroxypropyl)amine, di(2-hydroxypropyl)amine, monomethylaminoethanol, monoethylaminoethanol, monoethylaminobutanol, etc.; alkylene polyamines and ketiminized compounds of these polyamines such as ethylenediamine, propylenediamine, butylenediamine, hexamethylenediamine, tetraethylenepentamine, pentaethylenehexamine, diethylaminopropylamine, diethylenetriamine, triethylenetetramine, etc.; alkyleneimines such as ethyleneimine, propyleneimine, etc.; cyclic amines such as piperazine, morpholine, pyrazine, etc. Among the above-mentioned amines, it is also possible to use as amine compound (A2), ketiminized amines obtained by ketiminizing primary amines (for example, ketimine of diethylenetriamine with methyl isobutyl ketone, etc.). Amines obtained by ketiminizing primary amines can be used in combination with the amines listed above.

The proportion of each component used in the aforementioned addition reaction of modified epoxy resin (A1) and amine compound (A2) is not strictly limited, and can be suitably determined according to the use etc., of the cationic electrodeposition coating composition. The proportion of modified epoxy resin (A1) is 70 to 98 mass %, preferably 75 to 96 mass %, and the proportion of amine compound (A2) is 2 to 30 mass %, preferably 4 to 25 mass %, based on the total solids mass of modified epoxy resin (A1) and amine compound (A2) used in the production of amino group-containing modified epoxy resin (A).

The addition reaction is usually carried out in a suitable solvent at 80° C. to 170° C., and preferably 90° C. to 150° C. for 1 to 6 hours, and preferably 1 to 5 hours. Examples of the solvent used in the above reaction include hydrocarbon-based solvents such as toluene, xylene, cyclohexane, n-hexane, etc.; ester-based solvents such as methyl acetate, ethyl acetate, butyl acetate, etc.; ketone-based solvents such as acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl amyl ketone, etc.; amide-based solvents such as dimethylformamide, dimethylacetamide, etc.; alcohol-based solvents such as methanol, ethanol, n-propanol, iso-propanol, etc.; aromatic alkyl alcohol-based solvents such as phenyl carbinol, methyl phenyl carbinol, etc.; ether alcohol-based solvents such as ethylene glycol monobutyl ether, diethylene glycol monoethyl ether, etc.; and mixtures thereof, etc.

Blocked Polyisocyanate Curing Agent (B)

The combination use of amino group-containing modified epoxy resin (A) with blocked polyisocyanate curing agent (B) can provide a heat curable cationic electrodeposition coating composition.

Blocked polyisocyanate curing agent (B) is an addition-reaction product in almost stoichiometric amount of a polyisocyanate compound and an isocyanate blocking agent. Polyisocyanate compounds usable in blocked polyisocyanate curing agent (B) may be known compounds. Examples thereof include aromatic, aliphatic or alicyclic polyisocyanate compounds such as tolylene diisocyanate, xylylene diisocyanate, phenylene diisocyanate, diphenylmethane-2,2′-diisocyanate, diphenylmethane-2,4′-diisocyanate, diphenylmethane-4,4′-diisocyanate, crude MDI (polymethylene polyphenyl isocyanate), bis(isocyanatemethyl)cyclohexane, tetramethylene diisocyanate, hexamethylene diisocyanate, methylene diisocyanate, isophorone diisocyanate, etc.; cyclopolymers or biurets of these polyisocyanate compounds; and combinations thereof.

Specifically, tolylene diisocyanate, xylylene diisocyanate, phenylene diisocyanate, diphenylmethane-2,4′-diisocyanate, diphenylmethane-4,4′-diisocyanate, crude MDI, and like aromatic polyisocyanate compounds are particularly preferable in view of anti-corrosion properties.

The isocyanate blocking agent is added to isocyanate groups of a polyisocyanate compound to block the isocyanate groups. The blocked polyisocyanate compound obtained by such an addition is stable at room temperature; however, it is desirable that the blocking agent be dissociated to regenerate free isocyanate groups, when heated to the baking temperature of a coating film (usually about 100° C. to about 200° C.).

Examples of blocking agents usable in blocked polyisocyanate curing agent (B) include methylethylketoxime, cyclohexanone oxime and like oxime-based compounds; phenol, para-t-butylphenol, cresol and like phenol-based compounds; n-butanol, 2-ethylhexanol and like aliphatic alcohol-based compounds; phenylcarbinol, methylphenylcarbinol and like aromatic alkyl alcohol-based compounds; ethylene glycol monobutyl ether, diethylene glycol monoethyl ether and like ether alcohol-based compounds; ε-caprolactam, γ-butyrolactam and like lactam-based compounds; etc.

Phenol Resin (C)

Phenol resin (C) is a resin obtained by subjecting a phenol-based compound such as phenol, cresol, bisphenol A, etc. and an aldehyde-based compound such as formaldehyde etc. to a condensation reaction in the presence of an acid catalyst, basic catalyst, or the like. Of these, resins condensed by an acid catalyst are referred to as novolac phenol resins; and resins condensed by a basic catalyst are referred to as resol phenol resins.

In the present invention, both novolac phenol resins and resol phenol resins can be used. Usable resins include resins obtained by introducing a methylol group, and phenol resins in which the introduced methylol group is partially or wholly alkyl-etherified with an alcohol having 6 or less carbon atoms.

To improve adhesion of the resulting coating film, and obtain a coating film having excellent anti-corrosion properties on an untreated steel sheet even when the formed film is a thin film with a thickness of 15 μm or less, phenol resin (C) used in the present invention preferably has a hydroxy value of 90 to 623 mg KOH/g.

Commercially available phenol resin (C) includes SUMILITERESIN PR-HF-3, SUMILITERESIN PR-HF-6, SUMILITERESIN PR-53194, SUMILITERESIN PR-53195, SUMILITERESIN PR-54869, SUMILITERESIN PR-16382, SUMILITERESIN PR-51939, SUMILITERESIN PR-53153, SUMILITERESIN PR-53364, SUMILITERESIN PR-53365, and SUMILITERESIN PR-50702 (all produced by Sumitomo Bakelite Co., Ltd.); PHENOLITE TD-2131, PHENOLITE TD-2106, PHENOLITE TD-2093, PHENOLITE TD-2091, PHENOLITE TD-2090, PHENOLITE VH-4150, PHENOLITE VH-4170, PHENOLITE VH-4240, PHENOLITE KH-1160, PHENOLITE KH-1163, PHENOLITE KH-1165, PHENOLITE TD-2093-60M, PHENOLITE TD-2090-60M, PHENOLITE LF-4711, PHENOLITE LF-6161, PHENOLITE LF-4871, PHENOLITE LA-7052, PHENOLITE LA-7054, PHENOLITE LA-7751, PHENOLITE LA-1356, and PHENOLITE LA-3018-50P (produced by DIC Corporation); Shonol BRG-555, Shonol BRG-556, Shonol BRG-558, Shonol CKM-923, Shonol CKM-983, Shonol BKM-2620, Shonol BRL-2854, Shonol BRG-5590M, Shonol CKS-3898, Shonol CKS-3877A, and Shonol CKM-937 (produced by “Showa Highpolymer Co., Ltd”); Maruka Lyncur M-S-1, Maruka Lyncur M-S-2, Maruka Lyncur M-S-3, and Maruka Lyncur CST (produced by “Maruzen Petrochemical Co., Ltd.”); Nikanol NP-100, Nikanol P-100, Nikanol HP-150, Nikanol PR-1440 (produced by FUDOW Co., Ltd.), etc.

In the cationic electrodeposition coating composition of the present invention, it is preferable that amino group-containing modified epoxy resin (A) be contained in an amount of 30 to 75 parts by mass, preferably 30 to 65 parts by mass, blocked polyisocyanate curing agent (B) be contained in an amount of 10 to 40 parts by mass, preferably 10 to 35 parts by mass, and phenol resin (C) be contained in an amount of 3 to 35 parts by mass, preferably 4 to 32 parts by mass, per 100 parts by mass of the total solids content of the components (A), (B), and (C). Each component in the above range is preferable to improve the anti-corrosion properties of the coating film on the untreated steel sheet.

Metal Compound (D)

The cationic electrodeposition coating composition of the present invention comprises metal compound (D). Metal compound (D) is a compound of at least one metal (d) selected from the group consisting of zirconium, titanium, cobalt, vanadium, tungsten, molybdenum, copper, indium, zinc, aluminum, bismuth, yttrium, lanthanide metals, alkali metals, and alkali earth metals. Of these, water-soluble metal compounds are preferable.

Examples of zirconium compounds include zirconium chloride, zirconyl chloride, zirconium sulfate, zirconyl sulfate, zirconium nitrate, zirconyl nitrate, zirconium hydrofluoric acid, zirconium hydrofluoric acid salts, zirconium oxide, zirconyl bromide, zirconyl acetate, zirconyl carbonate, zirconium fluoride, etc.

Examples of titanium compounds include titanium chloride, titanium sulfate, titanyl sulfate, titanium nitrate, titanyl nitrate, titanium hydrofluoric acid, titanium hydrofluoric acid salts, titanium oxide, titanium fluoride, etc.

Examples of cobalt compounds include cobalt chloride, cobalt bromide, cobalt iodide, cobalt nitrate, cobalt sulfate, cobalt acetate, ammonium cobalt sulfate, etc. Of these, cobalt nitrate is particularly preferred.

Examples of vanadium compounds include lithium orthovanadate, sodium orthovanadate, lithium metavanadate, potassium metavanadate, sodium metavanadate, ammonium metavanadate, sodium pyrovanadate, vanadyl chloride, vanadyl sulfate, etc.

Examples of tungsten compounds include lithium tungstate, sodium tungstate, potassium tungstate, ammonium tungstate, sodium metatungstate, sodium paratungstate, ammonium pentatungstate, ammonium heptatungstate, sodium phosphotungstate, barium borotungstate, etc.

Examples of molybdenum compounds include lithium molybdate, sodium molybdate, potassium molybdate, ammonium heptamolybdate, calcium molybdate, magnesium molybdate, strontium molybdate, barium molybdate, phosphomolybdate, sodium phosphomolybdate, zinc phosphomolybdate, etc.

Examples of copper compounds include copper sulfate, copper(II) nitrate trihydrate, copper(II) ammonium sulfate hexahydrate, copper (II) oxide, copper phosphate, etc.

Examples of indium compounds include ammonium indium nitrate etc.

Examples of zinc compounds include zinc acetate, zinc lactate, zinc oxide, zinc nitrate, etc.

Examples of aluminum compounds include aluminum nitrate etc.

Examples of bismuth compounds include inorganic bismuth-containing compounds such as bismuth chloride, bismuth oxychloride, bismuth bromide, bismuth silicate, bismuth hydroxide, bismuth trioxide, bismuth nitrate, bismuth nitrite, bismuth oxycarbonate, etc.; and bismuth lactate, triphenylbismuth, bismuth gallate, bismuth benzoate, bismuth citrate, bismuth methoxyacetate, bismuth acetate, bismuth formate, bismuth 2,2-dimethylolpropionate, etc.

Examples of yttrium compounds include yttrium nitrate, yttrium formate, yttrium acetate, yttrium chloride, yttrium sulfamate, yttrium lactate, yttrium hypophosphite, etc.

Examples of lanthanoid metal compounds include lanthanum compounds such as lanthanum nitrate, lanthanum fluoride, lanthanum acetate, lanthanum boride, lanthanum phosphate, and lanthanum carbonate; cerium compounds such as cerium nitrate, cerium chloride, cerium acetate, cerium formate, cerium lactate, cerium oxalate, cerium ammonium nitrate, cerium sulfamate, diammonium cerium nitrate, and cerium hypophosphite; praseodymium compounds such as praseodymium nitrate, praseodymium sulfate, praseodymium formate, praseodymium acetate, praseodymium sulfate, praseodymium oxalate, and praseodymium hypophosphate; neodymium compounds such as neodymium nitrate, neodymium formate, neodymium acetate, neodymium lactate, neodymium sulfamate, neodymium oxide, and neodymium hypophosphite; samarium compounds such as samarium acetate, samarium formate, and samarium sulfamate; etc.

Examples of compounds of alkali metals (at least one metal selected from the group consisting of lithium, sodium, potassium, rubidium, cesium, and francium) include lithium tungstate, sodium tungstate, potassium tungstate, etc.

Examples of compounds of alkaline earth metals (at least one metal selected from the group consisting of beryllium, magnesium, calcium, strontium, barium, and radium) include calcium molybdate, magnesium molybdate, strontium molybdate, barium molybdate, etc.

In a preferable embodiment, the following are usable as metal compound (D), which is contained in the cationic electrodeposition coating composition of the present invention:

(1): compounds of at least one metal (d) selected from the group consisting of zirconium, titanium, cobalt, vanadium, tungsten, molybdenum, copper, indium, zinc, aluminum, bismuth, yttrium, lanthanide metals, alkali metals, and alkali earth metals.

(2): compounds consisting of a zirconium compound, or a combination of a zirconium compound and a compound of at least one metal (d) selected from the group consisting of titanium, cobalt, vanadium, tungsten, molybdenum, copper, indium, zinc, aluminum, bismuth, yttrium, lanthanide metals, alkali metals, and alkali earth metals. (3): compounds consisting of a combination of at least one compound selected from zirconium compounds and titanium compounds, and a compound of at least one metal selected from the group consisting of cobalt, vanadium, tungsten, molybdenum, copper, indium, zinc, aluminum, bismuth, yttrium, lanthanide metals, alkali metals, and alkali earth metals.

To improve the anti-corrosion properties on the untreated steel sheet, the amount of metal compound (D) used in the present invention is 10 to 10,000 ppm, and preferably 20 to 8,000 ppm calculated as metal, relative to the mass of the cationic electrodeposition coating composition.

Adding metal compound (D) so that the mass of metal is within the above-mentioned range is preferable to improve the anti-corrosion properties of the film on the untreated steel sheet without severely impairing coating composition stability even in the case that the formed coating film is a thin film with a thickness of 15 μm or less (when dried). Among metal compound (D), if metal nitrate is used, examples of the cationic electrodeposition coating composition of the present invention include those in which metal compound (D) is added to a solvent as well as those in which metal (d) and nitrogen oxide ion (E) are added to a solvent.

Nitrogen Oxide Ion (E)

The cationic electrodeposition coating composition of the present invention comprises nitrogen oxide ion (E). Nitrogen oxide ion (E) is a general term for nitrate ion, nitrite ion, etc. Examples of the cationic electrodeposition coating composition of the present invention include those in which a nitrogen oxide ion is added to a solvent etc., as well as those in which a compound that generates or contains a nitrogen oxide ion is added, thereby containing a nitrogen oxide ion in the cationic electrodeposition coating composition. Examples of compounds that generate or contain a nitrogen oxide ion include nitric acid, metal nitrate, metal nitrite, etc.

Examples of nitric acid, metal nitrate, and metal nitrite include nitric acid, nitrous acid, zinc nitrate, aluminum nitrate, ytterbium nitrate, yttrium nitrate, indium nitrate, molybdenum nitrate, potassium nitrate, calcium nitrate, silver nitrate, cobalt nitrate, zirconium nitrate, zirconyl nitrate, strontium nitrate, cesium nitrate, cerium nitrate, titanyl nitrate, titanium nitrate, iron nitrate, copper nitrate, samarium nitrate, neodium nitrate, praseodymium nitrate, ruthenium nitrate, lanthanum nitrate, copper nitrate, bismuth nitrate, magnesium nitrate, zinc nitrite, potassium nitrite, calcium nitrite, cerium nitrite, cupric nitrite, copper nitrite, barium nitrite, nickel nitrite, magnesium nitrite, etc.

The cationic electrodeposition coating composition can include nitrogen oxide ion (E) by adding at least one member selected from the nitric acids, metal nitrates, and metal nitrites listed above. The amount of nitrogen oxide ion (E) in a bath of the cationic electrodeposition coating composition of the present invention is 50 to 10,000 ppm, preferably 100 to 8,000 ppm, relative to the mass of the cationic electrodeposition coating composition (bath). Adjusting the amount of nitrogen oxide ion (E) to the above range is preferable because the deposition of metal compound (D) on the interface (substrate side) between the substrate and the film can be accelerated without impairing composition stability. For this reason, the anti-corrosion properties of the film on the untreated metal sheet can be improved even when the formed coating film is a thin film with a thickness of 15 μm or less (when dried).

The cationic electrodeposition coating composition of the present invention comprises, if necessary, other additives, such as pigments, catalysts, organic solvents, pigment dispersants, surface control agents, surfactants, etc., in amounts generally used in the field of coating compositions. Examples of the pigments and solvents include coloring pigments such as titanium white, carbon black, etc.; extender pigments such as clay, talc, baryta, etc.; rust-preventive pigments such as aluminum dihydrogen tripolyphosphate, aluminum phosphomolybdate, etc.; bismuth compounds such as bismuth oxide, bismuth hydroxide, bismuth lactate, etc.; organic tin compounds such as dibutyltin oxide, dioctyltin oxide, etc.; dialkyl tin aliphatic or aromatic carboxylates, such as dibutyltin dilaurete, dioctyltin dilaurete, dibutyltin diacetate, dioctyltin dibenzoate, dibutyl tin dibenzoate, etc.

The cationic electrodeposition coating composition of the present invention can be produced by the following methods (1) to (3).

Method (1): Amino group-containing modified epoxy resin (A), blocked polyisocyanate curing agent (B), phenol resin (C), and, if necessary, other additives are added and fully mixed to form a dissolution varnish. A neutralizer selected from the group consisting of formic acid, acetic acid, lactic acid, propionic acid, citric acid, malic acid, sulfamic acid, and mixtures of two or more of these acids is added to the dissolution varnish, and dispersed in an aqueous medium, thereby obtaining an emulsion. Metal compound (D) and nitrogen oxide ion (E) are then added to the emulsion, followed by further addition of pigment dispersion paste. Method (2): Metal compound (D) and nitrogen oxide ion (E) are mixed. A pigment ingredient, catalyst, other additives, water, etc. are added and dispersed in the mixture, thereby forming a pigment dispersion paste. The pigment dispersion paste is added to an emulsion containing amino group-containing modified epoxy resin (A), blocked polyisocyanate curing agent (B), and phenol resin (C). Method (3): Metal compound (D) and nitrogen oxide ion (E) are added to the bath of the previously prepared cationic electrodeposition coating composition (containing amino group-containing modified epoxy resin (A), blocked polyisocyanate curing agent (B), and phenol resin (C)), and diluted with water.

The cationic electrodeposition coating composition can be formed by the aforementioned methods (1) to (3), and like equivalent methods.

The cationic electrodeposition coating composition can be produced by adjusting the emulsion and pigment dispersion paste with deionized water etc., so that the solids content of Bath paint is 5 to 40 mass %, preferably 8 to 25 mass %, and the pH is 1.0 to 9.0, preferably 3.0 to 6.5.

There is no particular limitation on the method for producing a coating film using the cationic electrodeposition coating composition of the present invention, and any known methods can be used. For example, a coating film can be formed by applying a current to a substrate immediately after immersing the substrate in the bath of the cationic electrodeposition coating composition, (referred to as “a one-step method”), or by immersing a substrate in the bath of the cationic electrodeposition coating composition for a certain period, or performing electrocrystallization (performing electrodeposition coating at low voltage), followed by electrodeposition coating (referred to as a two-step method).

Of the aforementioned two methods, since the method comprising immersing the substrate in the bath containing the cationic electrodeposition coating composition of the present invention (Step 1), and then performing electrodeposition coating (Step 2) can provide a dense passivation film, such a method is preferable in view of improving anti-corrosion properties.

In the above described “two-step method”, a film can be formed by immersing the metal substrate in the bath containing the cationic electrodeposition coating composition at a temperature of 15° C. to 55° C., preferably 20° C. to 50° C. By immersing the substrate for 10 to 600 seconds, preferably 30 to 480 seconds, and more preferably 40 to 300 seconds (Step 1), a dense passivation film can be formed on the substrate.

Subsequently, by applying an electric current at a voltage of 50 to 400 V, preferably 75 to 370 V, for 60 to 600 seconds, preferably 80 to 400 seconds (Step 2) using the metal substrate as a cathode, a film can be deposited on the substrate.

It is preferable to set the temperature of the bath containing the cationic electrodeposition coating composition to 10° C. to 55° C., and particularly 20° C. to 50° C. since a deposition film having few defects can be uniformly formed. It is also possible to immerse the metal substrate in the electrodeposition coating composition bath, take the immersed metal substrate out of the bath, and then reimmerse the metal substrate in the bath to perform electrodeposition coating.

The two-step coating film production method can sequentially form on the first layer film (lower layer), the second layer film (upper layer) that mainly comprises a resin component, pigment, etc., which are completely different compositions from those of the first layer film, thereby providing a multiple layer film structure having excellent anti-corrosion properties and finish.

The mechanism for depositing the film using the cationic electrodeposition coating composition is as follows.

When immersion is conducted in Step 1, the pH in the vicinity of the substrate is raised by the etching effect of the nitric acid root contained in the cationic electrodeposition coating composition, and metal ions (for example, zirconium hexafluoride ion etc.) affected by the hydrolysis reaction cause a poorly-soluble film (lower layer) (mainly, for example, zirconium oxide) to be deposited on the substrate.

The thus obtained coating film is baked and heated at a surface temperature of the substrate of 100° C. to 200° C., preferably 120° C. to 180° C. for 5 to 90 minutes, preferably 10 to 50 minutes.

EXAMPLES

The present invention is explained in detail below with reference to production examples, examples, and comparative examples; however, the present invention is not limited thereto. In the examples, “parts” “and “%” are by mass.

Production of Amino Group-Containing Modified Epoxy Resin (A) Production Example 1 Production Example of Base Resin No. 1

A 2-liter flask equipped with a thermometer, a reflux condenser, and a stirrer was charged with 296 parts of Glyci-ale PP-300P (Note 1), 1,330 parts of jER828EL (Note 4), 684 parts of bisphenol A, and 1.0 parts of tetrabutylammonium bromide. The mixture was allowed to react at 160° C. until the epoxy equivalent became 1,150.

Next, 611 parts of methyl isobutyl ketone, and then 137 parts of monomethylaminoethanol were added to the reaction mixture, and allowed to react at 120° C. for 4 hours. The solution of base resin No. 1, which was an amino group-containing modified epoxy resin with a resin solids content of 80%, was thus obtained. Base resin No. 1 had an amine value of 41 mg KOH/g, and a number average molecular weight of 2,700.

Production Example 2 Production Example of Base Resin No. 2

A 2-liter flask equipped with a thermometer, a reflux condenser, and a stirrer was charged with 185 parts of Denacol EX-821 (Note 2), 950 parts of jER828EL (Note 4), 456 parts of bisphenol A, and 0.8 parts of tetrabutylammonium bromide. The mixture was allowed to react at 160° C. until the epoxy equivalent became 795.

Next, 368 parts of methyl isobutyl ketone, and then 110 parts of diethyl amine, and 95 parts of a ketimine of diethylenetriamine with methyl isobutyl ketone (purity: 84%, methyl isobutyl ketone solution) were added to the reaction mixture, and allowed to react at 120° C. for 4 hours. The solution of base resin No. 2, which was an amino group-containing modified epoxy resin with a resin solids content of 80%, was thus obtained. Base resin No. 2 had an amine value of 68 mg KOH/g, and a number average molecular weight of 2,000.

Production Example 3 Production Example of Base Resin No. 3

A 2-liter flask equipped with a thermometer, a reflux condenser, and a stirrer was charged with 340 parts of Glyci-ale BPP-350 (Note 3), 950 parts of jER828EL (Note 4), 456 parts of bisphenol A, and 0.8 parts of tetrabutylammonium bromide. The mixture was allowed to react at 160° C. until the epoxy equivalent became 873.

Next, 407 parts of methyl isobutyl ketone, and then 113 parts of monomethylaminoethanol, and 95 parts of a ketimine of diethylenetriamine with methyl isobutyl ketone (purity: 84%, methyl isobutyl ketone solution) were added to the reaction mixture, and allowed to react at 120° C. for 4 hours. The solution of base resin No. 3, which was an amino group-containing modified epoxy resin with a resin solids content of 80%, was thus obtained. Base resin No. 3 had an amine value of 62 mg KOH/g, and a number average molecular weight of 2,200.

Production Example 4 Production Example of Base Resin No. 4

A 2-liter flask equipped with a thermometer, a reflux condenser, and a stirrer was charged with 296 parts of Glyci-ale PP-300P (Note 1), 1,330 parts of jER828EL (Note 4), 684 parts of bisphenol A, and 1.0 parts of tetrabutylammonium bromide. The mixture was allowed to react at 160° C. until the epoxy equivalent became 1,150.

Next, 611 parts of propylene glycol monomethyl ether, and then 20 parts of diethylaminopropylamine, and 114 parts of monomethylaminoethanol were added to the reaction mixture, and allowed to react at 120° C. for 4 hours. The solution of base resin No. 4, which was an amino group-containing modified epoxy resin with a resin solids content of 80%, was thus obtained. The base resin No. 4 had an amine value of 41 mg KOH/g, and a number average molecular weight of 2,700.

Table 1 shows the formulations and the characteristic values of base resins Nos. 1 to 4 obtained in Production Examples 1 to 4.

TABLE 1 Production Production Production Production Example 1 Example 2 Example 3 Example 4 Base resin No. 1 No. 2 No. 3 No. 4 Formulation (A1) (a1) Glyci-ale PP-300P (Note 1) 296 296 Denacol EX-821 (Note 2) 185 Glyci-ale BPP-350 (Note 3) 340 (a2) jER828EL (Note 4) 1330 950 950 1330 (a3) Bisphenol A 684 456 456 684 Catalyst Tetrabutylammonium bromide 1.0 0.8 0.8 1.0 Solvent Methyl isobutyl ketone 368 407 Propylene glycol monomethyl 611 611 ether (A2) Mono methyl amino ethanol 137 113 114 Diethyl amino propyl amine 20 Diethyl amine 110 Ketimine of 95 95 diethylenetriamine with methyl isobutyl ketone Characteristic Amine value (mg KOH/g) 41 68 62 41 value Number average molecular weight 2700 2000 2200 2700 The numerals in the formulations are by parts. (Note 1) Glyci-ale PP-300P: trade name of an epoxy resin (diepoxy compound (a1)) produced by Sanyo Chemical Industries, Ltd.; epoxy equivalent: 296; corresponding to compound (2) (R³ = CH₃, X = 1, Y = 7) (Note 2) Denacol EX-821: trade name of an epoxy resin (diepoxy compound (a1)) produced by Nagase ChemteX Corporation; epoxy equivalent: 185; corresponding to compound (2) (R³ = hydrogen atom, X = 1, Y = 4) (Note 3) Glyci-ale BPP-350: trade name of an epoxy resin (diepoxy compound (a1)) produced by Sanyo Chemical Industries, Ltd.; epoxy equivalent: 340; corresponding to compound (1) (R¹ = CH₃, R² = CH₃, m + n = 3) (Note 4) jER828EL: trade name of an epoxy resin (a2) produced by Japan Epoxy Resin; epoxy equivalent: 190; number average molecular weight: 380

Synthesis Example 1 Production of Xylene-Formaldehyde Resin

A 2-liter separable flask equipped with a thermometer, a reflux condenser, and a stirrer was charged with 480 parts of 50% formalin, 110 parts of phenol, 202 parts of 98% industrial sulfuric acid, and 424 parts of m-xylene. The resulting mixture was allowed to react at 84° C. to 88° C. for 4 hours. After the reaction was completed, the reaction mixture was allowed to stand to separate a resin phase and a sulfuric acid aqueous phase. The resin phase was washed with water 3 times, and then unreacted m-xylene was removed under the conditions of 20 to 30 mmHg and 120° C. to 130° C. for 20 minutes. As a result, 480 parts of a phenol-modified xylene-formaldehyde resin having a viscosity of 1,050 mPa·s (25° C.) were obtained.

Production Example 5 Production Example of Base Resin No. 5

A flask was charged with 1,140 parts of jER828EL (Note 4), 456 parts of bisphenol A, and 0.2 parts of dimethylbenzylamine. The mixture was allowed to react at 130° C. until the epoxy equivalent became 820.

Next, 420 parts of methylisobutylketone, and then 300 parts of the xylene-formaldehyde resin obtained in Synthesis Example 1 were added to the reaction mixture. 95 parts of diethanol amine and 127 parts of a ketimine of diethylenetriamine with methyl isobutyl ketone (purity: 84%, methyl isobutyl ketone solution) were then added to the resulting mixture and allowed to react at 120° C. for 4 hours. The solution of base resin No. 5, which was an amino group-containing modified epoxy resin with a resin solids content of 80%, was thus obtained. Base resin No. 5 had an amine value of 47 mg KOH/g, and a number average molecular weight of 2,500.

Production of Blocked Polyisocyanate Curing Agent (B) Production Example 6 Production Example of Curing Agent

270 parts of Cosmonate M-200 (trade name of crude MDI produced by Mitsui Chemicals, Inc.) and 127 parts of methyl isobutyl ketone were added to a reaction vessel and heated to 70° C. 236 parts of ethylene glycol monobutyl ether were added dropwise over 1 hour, and the mixture was heated to 100° C. The mixture was sampled over time while the temperature was maintained; when no absorption by unreacted isocyanate groups was observed by infrared absorption spectrometry, a curing agent with a resin solids content of 80% was obtained.

Production Example 7 Production Example of Resin for Pigment Dispersion

1,010 parts of jER828EL (See Note 4) were blended with 390 parts of bisphenol A, 240 parts of PLACCEL 212 (trade name of polycaprolactonediol produced by Daicel Chemical Industries; weight average molecular weight: about 1,250) and 0.2 parts of dimethylbenzylamine, and the mixture was allowed to react at 130° C. until the epoxy equivalent became about 1,090.

Next, 134 parts of dimethylethanolamine and 150 parts of a 90% aqueous lactic acid solution were added to the reaction mixture, and then allowed to react at 120° C. for 4 hours. Methyl isobutyl ketone was subsequently added to the reaction mixture to adjust the solids content, thereby obtaining an ammonium salt-type resin for pigment dispersion having a solids content of 60%. The ammonium salt-type resin for pigment dispersion had an ammonium salt concentration of 0.78 mmol/g.

Production Example 8 Production Example of Pigment Dispersion Paste

8.3 parts (solids content: 5 parts) of the resin for pigment dispersion having a solids content of 60% that were obtained in Production Example 7, 14.5 parts of titanium oxide, 7.0 parts of refined clay, 0.3 parts of carbon black, 1 part of dioctyltin oxide, 1 part of bismuth hydroxide, and 20.3 parts of deionized water were added into a ball mill and dispersed for 20 hours. A pigment dispersion paste with a solids content of 55% was thus obtained.

Production of Emulsion Production Example 9 Production Example of Emulsion No. 1

81.3 parts (solids content: 65 parts) of base resin No. 1 obtained in Production Example 1 were mixed with 37.5 parts (solids content: 30 parts) of the curing agent obtained in Production Example 5 and 5 parts (solids content: 5 parts) of SUMILITERESIN PR-HF-3 (Note. 5). 15.0 parts of 10% acetic acid were further added to the resulting mixture and uniformly stirred. Thereafter, 155.2 parts of deionized water were added dropwise over about 15 minutes with vigorous stirring to thereby obtain emulsion No. 1 with a solids content of 34%.

Production Examples 10 to 17 Production Examples of Emulsions Nos. 2 to 9

Emulsions Nos. 2 to 9 were obtained in the same manner as in Production Example 9, except that the formulations shown in Table 2 were used.

TABLE 2 Pro. Pro. Pro. Pro. Pro. Pro. Pro. Pro. Exam. Pro. Exam. Exam. 9 Exam. 10 Exam. 11 Exam. 12 Exam. 13 Exam. 14 Exam. 15 16 17 Emulsion No. 1 No. 2 No. 3 No. 4 No. 5 No. 6 No. 7 No. 8 No. 9 Component A Base resin 81.3 81.3 81.3 68.8 87.5 No. 1 (65)   (65)   (65)   (55)   (70)   (solids content 80%) Base resin 81.3 No. 2 (65)   (solids content 80%) Base resin 81.3 No. 3 (65)   (solids content 80%) Base resin 81.3 No. 4 (65)   (solids content 80%) Base resin 81.3 No. 5 (65)   (solids content 80%) Component B Curing agent 37.5 37.5 37.5 37.5 37.5 37.5 37.5 37.5 37.5 (30)   (30)   (30)   (30)   (30)   (30)   (30)   (30)   (30)   Component C SUMILITERESIN  5.0  5.0  5.0  5.0  5.0 PR-HF-3 (Note 5) (5)  (5)  (5)  (5)  (5)  SUMILITERESIN  5.0 TD-2131 (Note 6) (5)  Shonol  5.0 15.0 BRG-555 (Note 7) (5)  (15)   10% Acetic acid 15.0 15.0 15.0 15.0 15.0 15.0 15.0 15.0 15.0 Deionized water 155.2  155.2  155.2  155.2  155.2  155.2  157.7  155.2  154.0  Total (Solids content 34%) 294.0  294.0  294.0  294.0  294.0  294.0  294.0  294.0  294.0  (100)   (100)   (100)   (100)   (100)   (100)   (100)   (100)   (100)   The parenthesized numerals in the formulations denote the solids content. (Note 5) SUMILITERESIN PR-HF-3: trade name of a phenol resin produced by Sumitomo Bakelite Co., Ltd.; hydroxy value: 539 mg KOH/g. (Note 6) PHENOLITE TD-2131: trade name of a phenol resin produced by DIC Corporation; hydroxy value: 539 mg KOH/g. (Note 7) Shonol BRG-555: trade name of a phenol resin produced by Showa Highpolymer Co., Ltd.; hydroxy value: 534 mg KOH/g.

Production of Cationic Electrodeposition Coating Composition Example 1

294 parts (solids content: 100 parts) of emulsion No. 1, 52.4 parts (solids content: 28.8 parts) of 55% pigment dispersion paste obtained in Production Example 8, and 653.6 parts of deionized water were mixed to obtain 1,000 parts of a bath. Subsequently, 6.8 parts of 10% zirconium hydrofluoric acid, and 10 parts of 10% nitric acid were added to the bath to obtain cationic electrodeposition coating composition No. 1.

Examples 2 to 28

Cationic electrodeposition coating compositions Nos. 2 to 28 were produced in the same manner as in Example 1, except that the formulations shown in Tables 3 to 5 were used.

TABLE 3 Exam. 1 Exam. 2 Exam. 3 Exam. 4 Exam. 5 Exam. 6 Exam. 7 Exam. 8 Cationic electrodeposition No. 1 No. 2 No. 3 No. 4 No. 5 No. 6 No. 7 No. 8 coating composition EM Emulsion No. 1 294.0 294.0 (100)   (100)   Emulsion No. 2 294.0 (100)   Emulsion No. 3 294.0 (100)   Emulsion No. 4 294.0 (100)   Emulsion No. 5 294.0 (100)   Emulsion No. 6 294.0 (100)   Emulsion No. 7 294.0 (100)   PP Pigment  52.4  52.4  52.4  52.4  52.4  52.4  52.4  52.4 dispersion  (28.8)  (28.8)  (28.8)  (28.8)  (28.8)  (28.8)  (28.8)  (28.8) paste Deionized water 653.6 653.6 653.6 653.6 653.6 653.6 653.6 653.6 Total (12.8% bath) 1000   1000   1000   1000   1000   1000   1000   1000   (128.8) (128.8) (128.8) (128.8) (128.8) (128.8) (128.8) (128.8) Component D 10% Zirconium  6.8  6.8  6.8  6.8  6.8  6.8  6.8 hydrofluoric   (0.68)   (0.68)   (0.68)   (0.68)   (0.68)   (0.68)   (0.68) acid H₂ZrF₆ 10% Titanium  10.3 hydrofluoric   (1.03) acid H₂TiF₆ Component E 10% Nitric  10.0  10.0  10.0  10.0  10.0  10.0  10.0  10.0 acid Relative to Mass of metal 300   300   300   300   300   300   300   300   the mass of of component the cationic D (ppm) electrodeposition Mass of 1000   1000   1000   1000   1000   1000   1000   1000   coating nitrogen composition oxide ion (ppm) The parenthesized numerals in the formulations denote the solids content.

TABLE 4 (continuation of Table 3) Ex. 9 Ex. 10 Ex. 11 Ex. 12 Ex. 13 Ex. 14 Cationic electrodeposition coating composition No. 9 No. 10 No. 11 No. 12 No. 13 No. 14 EM Emulsion No. 1 294.0 294.0 294.0 294.0 294.0 294.0 (100)   (100)   (100)   (100)   (100)   (100)   PP Pigment dispersion  52.4  52.4  52.4  52.4  52.4  52.4 paste  (28.8)  (28.8)  (28.8)  (28.8)  (28.8)  (28.8) Deionized water 653.6 653.6 653.6 653.6 653.6 653.6 Total (12.8% bath) 1000   1000   1000   1000   1000   1000   (128.8) (128.8) (128.8) (128.8) (128.8) (128.8) Component D 10% Zirconium hydrofluoric acid H₂ZrF₆ 10% Zirconyl nitrate ZrO(NO₃)₂  7.6   (0.76) 10% Zinc nitrate Zn(NO₃)₂  16.0  (1.6) 10% Yttrium nitrate Y(NO₃)₃  9.3   (0.93) 10% Cupric nitrate Cu(NO₃)₂  8.8   (0.88) 10% Ytterbium nitrate Yb(NO₃)₃  6.2   (0.62) 10% Cerium nitrate Ce(NO₃)₃  7.0  (0.7) 10% Indium nitrate In(NO₃)₃ 10% Bismuth nitrate Bi(NO₃)₃ Component E 10% Nitric acid  5.9  4.3  3.7  4.2  6.8  6.0 Relative Mass of metal of component D (ppm) 300   300   300   300   300   300   to the Mass of nitrogen oxide ion (ppm) 1000   1000   1000   1000   1000   1000   mass of the cationic electrode position coating composition Ex. 15 Ex. 16 Ex. 17 Ex. 18 Ex. 19 Ex. 20 Cationic electrodeposition coating composition No. 15 No. 16 No. 17 No. 18 No. 19 No. 20 EM Emulsion No. 1 294.0 294.0 294.0 294.0 294.0 294.0 (100)   (100)   (100)   (100)   (100)   (100)   PP Pigment dispersion  52.4  52.4  52.4  52.4  52.4  52.4 paste  (28.8)  (28.8)  (28.8)  (28.8)  (28.8)  (28.8) Deionized water 653.6 653.6 653.6 653.6 653.6 653.6 Total (12.8% bath) 1000   1000   1000   1000   1000   1000   (128.8) (128.8) (128.8) (128.8) (128.8) (128.8) Component D 10% Zirconium hydrofluoric acid  6.8  6.8  6.8  6.8 H₂ZrF₆   (0.68)   (0.68)   (0.68)   (0.68) 10% Zirconyl nitrate ZrO(NO₃)₂ 10% Zinc nitrate Zn(NO₃)₂  16.0  (1.6) 10% Yttrium nitrate Y(NO₃)₃  9.3   (0.93) 10% Cupric nitrate Cu(NO₃)₂ 10% Ytterbium nitrate Yb(NO₃)₃  6.2   (0.62) 10% Cerium nitrate Ce(NO₃)₃  7.0  (0.7) 10% Indium nitrate In(NO₃)₃  11.0  (1.1) 10% Bismuth nitrate Bi(NO₃)₃  5.7   (0.57) Component E 10% Nitric acid  5.1  7.3  4.3  3.7  6.8  6.0 Relative Mass of metal of component D (ppm) 300   300   600   600   600   600   to the Mass of nitrogen oxide ion (ppm) 1000   1000   1000   1000   1000   1000   mass of the cationic electrode position coating composition The parenthesized numerals denote the solids content.

TABLE 5 (continuation of Table 3) Ex. 21 Ex. 22 Ex. 23 Ex. 24 Ex. 25 Ex. 26 Ex. 27 Ex. 28 Cationic electrodeposition No. 21 No. 22 No. 23 No. 24 No. 25 No. 26 No. 27 No. 28 coating composition EM Emulsion No. 1   294.0   294.0   294.0   294.0   294.0   294.0   294.0   294.0 (100) (100) (100) (100) (100) (100) (100) (100) PP Pigment   52.4   52.4   52.4   52.4   52.4   52.4   52.4   52.4 dispersion   (28.8)   (28.8)   (28.8)   (28.8)   (28.8)   (28.8)   (28.8)   (28.8) paste Deionized water   653.6   653.6   653.6   653.6   653.6   653.6   653.6   653.6 Total (12.8% bath) 1000  1000  1000  1000  1000  1000  1000  1000    (128.8)   (128.8)   (128.8)   (128.8)   (128.8)   (128.8)   (128.8)   (128.8) Component D 10% Zirconium    6.8    6.8    6.8    6.8 hydrofluoric    (0.68)    (0.68)    (0.68)    (0.68) acid H₂ZrF₆ 10% Titanium   10.3 hydrofluoric    (1.03) acid H₂TiF₆ 10% Cobalt    9.3 nitrate    (0.93) Co(No₃)₂ 10%    7.0    7.0 Praseodymium    (0.7)    (0.7) nitrate Pr(No₃)₃ 10% Zinc    8.4 acetate    (0.84) Zn(CH₃COO)₂ 10% Cerium    6.8    6.8 acetate    (0.68)    (0.68) Ce(CH₃COO)₃ 10%    8.8 Neodymium    (0.88) acetate Nd(CH₃COO)₃ Component E 10% Nitric    3.7    6.0   0.0   10.0   10.0    6.0   10.0   10.0 acid Relative to Mass of metal 300 300 300 300 600 600 600 600 the mass of of component the cationic D (ppm) electrodeposition Mass of 1000  1000  1000  1000  1000  1000  1000  1000  coating nitrogen composition oxide ion (ppm) The parenthesized numerals in the formulations denote the solids content.

Comparative Examples 1 to 6

Cationic electrodeposition coating compositions Nos. 29 to 34 were produced in the same manner as in Example 1, except that the formulations shown in Table 6 were used.

TABLE 6 Comp. Comp. Comp. Comp. Comp. Comp. Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 Cationic electrodeposition No. 29 No. 30 No. 31 No. 32 No. 33 No. 34 coating composition EM Emulsion No. 1 294.0 294.0 294.0 294.0 (100)   (100)   (100)   (100)   Emulsion No. 8 294.0 (100)   Emulsion No. 9 294.0 (100)   PP Pigment  52.4  52.4  52.4  52.4  52.4  52.4 dispersion  (28.8)  (28.8)  (28.8)  (28.8)  (28.8)  (28.8) paste Deionized water 653.6 653.6 653.6 653.6 653.6 653.6 12.8% Bath 1000   1000   1000   1000   1000   1000   (128.8) (128.8) (128.8) (128.8) (128.8) (128.8) Component D 10% Zirconium  6.8  6.8  6.8  14.0 hydrofluoric   (0.68)   (0.68)   (0.68)  (1.4) acid H₂ZrF₆ 10% Titanium  10.3 hydrofluoric   (1.03) acid H₂TiF₆ Component E 10% Nitric  10.0  10.0 —  10.0 — — acid Relative to Mass of metal 300   300   300   — 300   600   the mass of of component D the cationic (ppm) electrodeposition Mass of 1000   1000   — 1000   — — coating nitrogen oxide composition ion The parenthesized numerals in the formulations denote the solids content. Substrate to be Coated

Cold rolled steel sheets (70 mm×150 mm×0.8 mm) that had not been subjected to chemical conversion treatment were immersed in an ultrasonic cleaner containing toluene, and subjected to ultrasonic degreasing for 30 minutes, thereby obtaining “substrates to be coated”.

Preparation and Evaluation of Test Sheets Containing Cationic Electrodeposition Coating Films

The temperature of each bath of cationic electrodeposition coating compositions Nos. 1 to 34 was adjusted to 40° C., and a “substrate to be coated” was immersed in a bath for 120 seconds (Step 1). Electrodeposition coating (Step 2) was then performed at 200V, for 180 seconds, and baking was conducted at 170° C. for 20 minutes, thereby obtaining a test sheet having a thickness of 15 μm (when dried). Each test sheet was evaluated according to the following conditions. Tables 7 to 9 show the results of the Examples, and Table 10 shows the results of the Comparative Examples.

TABLE 7 Example 1 Example 2 Example 3 Example 4 Example 5 Example 6 Example 7 Example 8 Cationic No. 1 No. 2 No. 3 No. 4 No. 5 No. 6 No. 7 No. 8 electrodeposition coating composition Finish (coating B B B B B B B B film condition) (Note 8) Hot salt water B B B B B B A B immersion resistance (Note 9) Exposure B B B B B B A B resistance (Note 10) Coating B B B B B B B B composition stability (Note 11) Comprehensive B B B B B B A B evaluation (Note 12)

TABLE 8 (continuation of Table 7) Ex. 9 Ex. 10 Ex. 11 Ex. 12 Ex. 13 Ex. 14 Ex. 15 Ex. 16 Ex. 17 Ex. 18 Ex. 19 Ex. 20 Cationic No. 9 No. 10 No. 11 No. 12 No. 13 No. 14 No. 15 No. 16 No. 17 No. 18 No. 19 No. 20 electrodeposition coating composition Finish (coating B B B B B B B B B B B B film condition) (Note 8) Hot salt water B B B B B B B B A A A A immersion resistance (Note 9) Exposure B B B B B B B B A A A A resistance (Note 10) Coating B B B B B B B B B B B B composition stability (Note 11) Comprehensive B B B B B B B B A A A A evaluation (Note 12)

TABLE 9 (continuation of Table 7) Example Example Example Example Example Example Example Example 21 22 23 24 25 26 27 28 Cationic No. 21 No. 22 No. 23 No. 24 No. 25 No. 26 No. 27 No. 28 electrodeposition coating composition Finish (coating B B B B B B B B film condition) (Note 8) Hot salt water B B B B B A A A immersion resistance (Note 9) Exposure B B B B B A A A resistance (Note 10) Coating B B B B B B B B composition stability (Note 11) Comprehensive B B B B B A A A evaluation (Note 12)

TABLE 10 Comp. Comp. Comp. Comp. Comp. Comp. Exam. 1 Exam. 2 Exam. 3 Exam. 4 Exam. 5 Exam. 6 Cationic No. 29 No. 30 No. 31 No. 32 No. 33 No. 34 electro- deposition coating composition Finish (coating B B — — — — film condition) (Note 8) Hot salt water D C C D C C immersion resistance (Note 9) Exposure D D C D C C resistance (Note 10) Coating D B B B B B composition stability (Note 11) Comprehensive D D D D D D evaluation (Note 12) (Note 8) Finish (condition of coating film): Each test sheet was cut, and the conditions of the coating films (lower layer and upper layer) were observed using HF-2000 (a field emission transmission electron microscope produced by Hitachi Ltd.) The conditions of the coating films were evaluated according to the following criteria. B: The boundary between the coating films (lower layer and upper layer) was unclear, but slight layer separation was observed. —: No layer separation was observed. (Note 9) Hot salt water immersion resistance: Each test sheet was immersed in 5 wt. % of salt water at 50° C. for 480 hours, and a Sellotape (trade name) peeling test was performed. The percentage (%) of the portion that peeled off was measured. A: The percentage of peeled portion relative to the whole coating film was less than 5%. B: The percentage of peeled portion relative to the whole coating film was not less than 5% and less than 10%. C: The percentage of peeled portion relative to the whole coating film was not less than 10% and less than 20%. D: The percentage of peeled portion relative to the whole coating film was not less than 20%. (Note 10) Exposure Resistance Test WP-300 (trade name of an aqueous intermediate coating composition produced by Kansai Paint Co., Ltd.) was sprayed over a test sheet obtained in the same manner as above to a cured film thickness of 25 μm, and then baked at 140° C. for 30 minutes using an electric hot air dryer. Thereafter, NEO AMILAC 6000 (trade name of a topcoat composition produced by Kansai Paint Co., Ltd.) was sprayed over the intermediate coating film to a cured film thickness of 35 μm. Baking was then conducted using an electric hot air dryer at 140° C. for 30 minutes, thereby obtaining an exposure test sheet. The coating film on the resulting exposure test sheet was cross-cut with a knife so that the cut reached the substrate. The sheet was placed flatly and exposed to outside weather conditions in Chikura-machi, Chiba Prefecture (beach side), for one year. The exposure resistance was then evaluated, based on the width of rust or blister from the cut portion. A: The maximum width of rust or blister from the cut was less than 2.0 mm (on one side). B: The maximum width of rust or blister from the cut was not less than 2.0 mm and less than 3.0 mm (on one side). C: The maximum width of rust or blister from the cut was not less than 3.0 mm and less than 4.0 mm (on one side). D: The maximum width of rust or blister from the cut was not less than 4.0 mm (on one side). (Note 11) Coating composition stability: Each of the film forming agents was sealed in a vessel at 30° C. for 30 minutes and then stirred. The total amount of film forming agent was filtered through a 400-mesh sieve. The amount of residue (mg/L) was measureded. B: less than 10 mg/L C: Not less than 10 mg/L, and less than 15 mg/L D: Not less than 15 mg/L (Note 12) Comprehensive evaluation: In the field of cationic electrodeposition coating compositions to which the present invention belongs, it is desirable that the cationic electrodeposition coating composition excel in terms of finish, hot salt water immersion resistance, exposure resistance, and coating composition stability. It is most desirable that the cationic electrodeposition coating composition receive the highest rating for all of the four properties (A is the highest rating for hot salt water immersion resistance, and exposure resistance; and B is the highest rating for finish and coating composition stability). Specifically, a comprehensive evaluation was conducted according to the following criteria: A: hot salt water immersion resistance and exposure resistance were rated as A, and finish and coating composition stability were rated as B. B: Four properties were rated as A or B, including not more than one A. C: Four properties were rated as A, B, or C, including at least one C. D: Of the four properties, at least one property was rated as D or “—”.

INDUSTRIAL APPLICABILITY

The present invention can provide a coated article that exhibits excellent anti-corrosion properties even on an untreated steel sheet. 

1. A cationic electrodeposition coating composition comprising amino group-containing modified epoxy resin (A), blocked polyisocyanate curing agent (B), phenol resin (C), metal compound (D), and nitrogen oxide ion (E); the cationic electrodeposition coating composition comprising the metal compound (D) in an amount of 10 to 10,000 ppm calculated as metal (on a metal mass basis) and the nitrogen oxide ion (E) in an amount of 50 to 10,000 ppm, relative to the mass of the cationic electrodeposition coating composition, the amino group-containing modified epoxy resin (A) being a resin obtained by reacting modified epoxy resin (A1) having an epoxy equivalent of 500 to 2,500 and amine compound (A2), the modified epoxy resin (A1) being obtained by reacting diepoxy compound (a1), epoxy resin (a2) having an epoxy equivalent of 170 to 500, and bisphenol compound (a3), the diepoxy compound (a1) being compound (1) represented by Formula (1) below,

wherein R¹ is the same or different, and each represents a hydrogen atom or a C₁₋₆ alkyl group; R² is the same or different, and each represents a hydrogen atom or C₁₋₂ alkyl group, and m and n, which represent the number of repeating units of the portion having an alkylene oxide structure, are integers where m+n=1 to 20, and/or compound (2) represented by Formula (2) below,

wherein R³ represents a hydrogen atom or C₁₋₆ alkyl group, X is an integer of 1 to 9, and Y is an integer of 1 to 50; when Y is 2 or more, each R³ in the repeating unit is the same or different, and the metal compound (D) being a compound of at least one metal (d) selected from the group consisting of zirconium, titanium, cobalt, vanadium, tungsten, molybdenum, copper, indium, zinc, aluminum, bismuth, yttrium, lanthanoids, alkali metals, and alkaline earth metals.
 2. The cationic electrodeposition coating composition according to claim 1, wherein the amino group-containing modified epoxy resin (A) is contained in an amount of 30 to 75 parts by mass, the blocked polyisocyanate curing agent (B) is contained in an amount of 10 to 40 parts by mass, and the phenol resin (C) is contained in an amount of 3 to 35 parts by mass, based on the total solids mass (100 parts by mass) of the amino group-containing modified epoxy resin (A), blocked polyisocyanate curing agent (B), and phenol resin (C).
 3. The cationic electrodeposition coating composition according to claim 1, wherein the modified epoxy resin (A1) is obtained by reacting 1 to 35 mass % of the diepoxy compound (a1), 10 to 80 mass % of the epoxy resin (a2), and 10 to 60 mass % of the bisphenol compound (a3), based on the total solids mass of the diepoxy compound (a1), epoxy resin (a2), and bisphenol compound (a3).
 4. The cationic electrodeposition coating composition according to claim 1, wherein R¹ in the Formula (1) or R³ in the Formula (2) is a methyl group or hydrogen atom.
 5. The cationic electrodeposition coating composition according to claim 1, wherein the metal compound (D) consists of a zirconium compound, or comprises at least one compound selected from the group consisting of zirconium compounds and titanium compounds, and a compound of at least one metal selected from the group consisting of cobalt, vanadium, tungsten, molybdenum, copper, indium, zinc, aluminum, bismuth, yttrium, lanthanoids, alkali metals, and alkaline earth metals.
 6. The cationic electrodeposition coating composition according to claim 1, wherein the solids content of the cationic electrodeposition coating composition is 5 to 40 mass %.
 7. A coated article obtained by immersing a metal substrate in an electrodeposition coating composition bath containing the cationic electrodeposition coating composition according to claim 1, and performing electrodeposition coating.
 8. The cationic electrodeposition coating composition according to claim 2, wherein the modified epoxy resin (A1) is obtained by reacting 1 to 35 mass % of the diepoxy compound (a1), 10 to 80 mass % of the epoxy resin (a2), and 10 to 60 mass % of the bisphenol compound (a3), based on the total solids mass of the diepoxy compound (a1), epoxy resin (a2), and bisphenol compound (a3).
 9. A coated article obtained by immersing a metal substrate in an electrodeposition coating composition bath containing the cationic electrodeposition coating composition according to claim 2, and performing electrodeposition coating.
 10. A coated article obtained by immersing a metal substrate in an electrodeposition coating composition bath containing the cationic electrodeposition coating composition according to claim 3, and performing electrodeposition coating.
 11. A coated article obtained by immersing a metal substrate in an electrodeposition coating composition bath containing the cationic electrodeposition coating composition according to claim 4, and performing electrodeposition coating.
 12. A coated article obtained by immersing a metal substrate in an electrodeposition coating composition bath containing the cationic electrodeposition coating composition according to claim 5, and performing electrodeposition coating.
 13. A coated article obtained by immersing a metal substrate in an electrodeposition coating composition bath containing the cationic electrodeposition coating composition according to claim 6, and performing electrodeposition coating.
 14. A coated article obtained by immersing a metal substrate in an electrodeposition coating composition bath containing the cationic electrodeposition coating composition according to claim 8, and performing electrodeposition coating. 